Selected for dental excellence

The 4DML Pure is engineered for implant-supported restorations, offering exceptional strength even at the center core

4DML Pure

Selected Dental 4DML Pure is developed to meet the highest standards of modern dentistry. Our discs are crafted with multilayered zirconia for optimal translucency and durability. Suitable for both anterior and posterior restorations. Available in:

VITA16 colour + bleached white (BL1-BL4, 0M1-0M3)
12~25 mm thickness
Diameter 98 mm and 95 mm

6 Layers Multilayer

Layer composition 14 mm disc

Our zirconia discs feature a gradient structure that mimics the natural translucency of enamel and dentin. The material transitions smoothly from high-opacity at the cervical area to high-translucency at the incisal edge, delivering a natural esthetic without the need for additional staining.

Multilayered composition for realistic depth
Optimal light transmission in esthetic zones
Consistent shade integration across layers

Visual Evaluation

We photographed our Zirconia together with the Vita shades for you.

Rules

Shade Matching Guides: Compare zirconia samples using VITA shade guides or custom shade tabs.
Lighting Conditions: Evaluate under multiple light sources (natural daylight, LED, fluorescent) to detect metamerism.
Background Color: Use a consistent and neutral background to minimize perception distortion.
Thickness: Ensure all samples are of equal thickness to allow fair visual comparison.

Discover the Results

Technichal Information

Dental Zirconia Block : 4D

Sintering Instructions

Show steps

Table

Notes: 
Both programs hold 120 min at 1500 °C; use controlled cooling thereafter.

Graph

Show steps

Table

Graph

Show steps

Table

Graph